UTILIZATION OF ACTIVATED CARBON FROM ELEPHANT GRASS (PENNISETUM PURPEREUM) AND MANGANESE DIOXIDE AS SUPERCAPACITOR ELECTRODES
DOI:
10.54443/morfai.v5i4.3146Published:
2025-06-12Downloads
Abstract
The growing need for sustainable and eco-friendly energy storage solutions has led to advancements in high-performance supercapacitors with extended cycle life. This research explores the fabrication of composite electrodes using activated carbon derived from elephant grass (Pennisetum purpureum) combined with manganese dioxide (MnO₂). The carbon material was produced through chemical activation with potassium hydroxide (KOH) and subsequent physical activation using carbon dioxide (CO₂). MnO₂ was incorporated into the activated carbon at various weight ratios (10:0, 7:3, 5:5, 3:7, and 0:10). Morphological and elemental analyses were performed using SEM-EDS, Meanwhile, the electrochemical performance was evaluated using galvanostatic charge-discharge (GCD) tests and electrochemical impedance spectroscopy (EIS). Of all the samples evaluated, the composite containing a 3:7 ratio of carbon to MnO₂ exhibited the highest specific capacitance, reaching 198.51 F/g, highlighting the beneficial interaction between double-layer capacitance and pseudocapacitance. These findings suggest that elephant grass-derived carbon, when effectively combined with MnO₂, presents a cost-effective and environmentally friendly option for next-generation supercapacitor electrodes.
Keywords:
Activated Carbon, Electrochemical Performance, Elephant Grass, Manganese Dioxide, SupercapacitorReferences
Y. Zhao, X. Sun, and J. Wang, “Thermal and chemical stability of NMP as a solvent in polymer processing,” Polymer Science Journal, vol. 45, no. 6, pp. 312–321, 2019.
Y. Wang et al., “Effect of MnO₂ loading on supercapacitor performance,” Materials Chemistry and Physics, vol. 220, pp. 78–89, 2021.
X. Zhang et al., “Recent progress in carbon-based electrodes for supercapacitors,” Energy Storage Materials, vol. 32, pp. 123–145, 2020.
J. Lee and D. Kim, “Nanostructured carbon materials for adsorption,” ACS Nano, vol. 15, no. 9, pp. 12345–12367, 2021.
J. Zhou et al., “MnO₂ electrode performance in asymmetric supercapacitors,” Journal of Materials Science, vol. 55, no. 12, pp. 4860–4872, 2020.
Y. Wang et al., “Pseudocapacitive properties of MnO₂ composites for energy storage applications,” Energy Storage Materials, vol. 14, no. 5, pp. 232–245, 2022.
Y. Zhang, X. Liu, and Q. Wang, “Understanding impedance behavior in electrochemical energy storage devices,” Journal of Electroanalytical Chemistry, vol. 860, p. 113884, 2020.
Y. Li et al., “MnO₂/carbon composites as high-performance electrodes for supercapacitors,” Journal of Power Sources, vol. 417, pp. 1–10, 2019.
License
Copyright (c) 2025 Erna Frida, Syahrul Humaidi, Fathi Marzuqi
This work is licensed under a Creative Commons Attribution 4.0 International License.
Downloads
How to Cite